410 Stainless Steel By Yaang Pipe Industry www.yaang.com

by yane Yang Sales Manager

Type 410 Stainless Steel is a martensitic stainless steel that provides good corrosion resistance plus high strength and hardness. It is magnetic in both the annealed and hardened conditions. A wide range of properties can be developed with different heat treatments.

Product Forms:

Stainless Steel Pipes, Stainless Steel Flanges, Stainless Steel Pipe Fittings, Strip Specifications: ASTM A240

Chemical Composition:

ElementType 410
Carbon0.08 – 0.15
Manganese1.00 max.
Sulfur0.030 max.
Phosphorus0.040 max.
Silicon1.00 max.
Chromium11.5 – 13.5
Nickel0.75 max.

​Mechanical Properties:

TypeYield Strength 0.2% offset (KSI)Tensile Strength (KSI)% Elongation (2" Gauge length)Hardness Rockwell
410 Ann30 min.65 min.20 min.HRB 96

Physical Properties:

Density (lb./ in^2) @ RT 0.28
Modulus of Elasticity in Tension (psi x 10^6) 29.0
Specific Heat (BTU/o F/lb.)32 to 212 oF0.11
Thermal Conductivity (BTU/hr/ft^2/ft)212oF14.4
 932oF16.6
Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F)32 to 212oF5.5
 32 to 1,200oF6.5
Electrical Resistivity (micro ohms - cm)at 70oF22.5

Typical Applications:

Collector rings, airplane exhaust stacks, annealing box covers, stainless steel flanges, stainless steel pipe fittingsjet engineparts,expansion joints, stainless steel tubes, stainless steel bars, stainless steel angle bars flexible metal hose and bellows.

Processing:

Annealing: Heat slowly to 1500 -1650°F, cool to 1100°F in furnace, air cool. Process Annealing: Heat to 1350 -1450°F, air cool. Hardening: Heat to 1700 - 1850°F, air cool or oil quench. Follow by stress-relief or temper. Stress Relieving: Heat at 300 - 800°F for 1 to 2 hours, air cool.

Tempering:

Heat to 1100 - 1400°F for 1 to 4 hours, air cool.

Forming:

Type 410 Stainless Steel has reasonably good cold working properties and can be moderately drawn and formed in the annealed condition.

Welding:

The martensitic alloys have limited weldability due to their hardenability. Corrosion: Type 410 Stainless Steel provides good corrosion resistance to air, water and some chemicals. It shows satisfactory resistance to nitric acid, concentrated sulfuric acid, dilute acetic acid and naphtha.

Source: Zhejiang Yaang Pipe Industry Co., Limited (www.yaang.com)


About yane Yang Senior     Sales Manager

144 connections, 0 recommendations, 657 honor points.
Joined APSense since, June 7th, 2014, From wenzhou, China.

Created on Dec 31st 1969 19:00. Viewed 0 times.

Comments

No comment, be the first to comment.
Please sign in before you comment.